|1. Low temperature cure to 25 F|
2. Excellent adhesion to tight rust
3. A high build primer or finish coat
4. Fast Recoating
5. Excellent against “undercutting”
6. Easy to apply, self priming on steel
7. Excellent build to protect sharp edges and crevices
8. Tight film, low permeability
9. Excellent chemical, abrasion and impact resistance
10. Excellent as a coating on concrete
11. Good adhesion to moist substrates
12. Excellent immersion resistance in fresh and salt water.
|Volume Solids||75% 2%|
|Theoretical Coverage (per gallon at 1.0 DFT.)||1203 ft|
|Recommended Thickness||4 – 7 dry mils at 170-300 sq. ft. per gallon, normally applied at 5 dry mils|
|Mixing Ratio||4:1 by volume. Mix 4 parts Base (Part A) to 1 part Hardener (Part B)|
|Induction Time||15 min|
|Pot Life||2 hours at 75 F|
|Thinning||5 – 15% SA-65 Reducer per gallon|
|Application||Spray, brash or roller|
|Application Temperature||25 to 120 F|
|Maximum Dry Service Temperature||200 F|
|Recoat Time||4 hours at 75 F (5 dry mils)|
|Packaging||1 gal. unit|
5 gal. units
|Excellent resistance against alkalis, salts, fresh or salt water, gasoline and many acids and solvents. PC-636 is recommended for coating in immersion in fresh and salt water, gasoline, diesel fuel and other chemicals.|
|Ideal for structural steel, tanks, vessels, water towers, cooling towers, equipment, lines and racks, metal buildings, fences, cat-walks, bridges, railings, fire escapes, etc., in chemical processing plants, pulp and paper mills, sewage and waste water treatment facilities, fertilizer plants, petroleum refineries, electric generating stations, coal handling operations, food processing plants, breweries, dairies, dams, locks, marine installations, etc.|
a. Sandblast – best
Sandblast to a “commercial” (SSPC-SP6-63) or “Near White” (SSPC-SP10-63) blast finish. For best results, prime same day with PC-636 or MCU-100 Aluminum.
b. Power Tool Clean
c. Hand Cleaning
2. Galvanized Steel
b. Old, Weathered or Rusty
3. Previously Painted Surfaces
All concrete should be prepared in accordance with the American Concrete Institute (ACI), Steel Structures Painting Council (SSPC) and National Association of Corrosion Engineers (NACE) concrete specifications. Remove all dirt, dust, oil, grease, laitance, efflorescence, loose or unsound concrete, and any chemical contaminants by such methods as high pressure water blast, wet or dry abrasive blast, vacuum shot blast, acid etching and other accepted surface preparation methods. A combination of these methods are normally used. Random pH readings using distilled water should be made to ensure all contaminants have been removed. A final pH reading of 7.0 – 8.5 is acceptable.
Coating System Concrete
|Mixing Instructions, Application Procedure & Recoat Time|
Stir each component to a uniform consistency, using an explosion proof variable speed drill with a Jiffy Mixer. Make sure any pigment settled to the bottom is incorporated. Do not vary proportions. PC-636 is prepared by mixing 4 parts Base (part A) to 1 part Hardener (Part B) with a power mixer. Allow an induction time of 15 minutes. PC-636 may be thinned up to 15% with SA-65 Thinner.
|PC-636 is Flammable. Keep away from all sources of ignition during mixing, application and cure. The Hardener (Part B) is also corrosive and can cause eye and skin irritation as well as allergic reactions. The use of goggles, fresh air masks or NIOSH approved respirators, protective skin cream and protective clothing is a recommended standard practice when spraying coatings. Proper ventilation is always required.|
This product is sold without warranty as to performance expressed or implied. Users are urged to make their own tests to determine the suitability for their particular conditions.
For Professional use only.
PC-636 Low Temperature Curing High Build Epoxy Coating
Poly-Chem PC-636 is a high performing, surface tolerant, two component, high solids, high build amine cured epoxy designed to cure at temperatures down to 25 F. PC-636 Epoxy is specially modified with a proprietary blend of selective resins, wetting agents and penetrants to provide excellent adhesion and protection of sound, rusty steel surfaces. Depending on the temperature, the fast setting PC-636 can be recoated the same day.