|Inorganic Acids||Very Good|
|Organic Acids||Very Good|
|Flexural Strength at 70 F||18800psi|
|Tensile Strength at 70 F||12100psi|
|Tensile Shear at 70 F||3000psi|
|Max. Dry Operating Temperature||400F|
|Operating pH Range||1.0 – 14.0|
|Packaging||1 kg unit|
4 kg units
|Mixing Ratio||2 parts base (B) to 1 part (A) hardener by volume|
5 parts base (B) to 2 part (A) hardener by weight
|For a 1 kg. unit, mix at 70 F, pot life is approximately 30 minutes. Higher temperatures or larger mass will shorten this time, lower temperatures or smaller mass will extend it. Pot life can also be extended by spreading the mass out to dissipate heat.|
|Storage||Store in dry area in closed containers between 50 F and 110 F. Shelf life at these conditions is greater than one year.|
|EAC has the consistency of a thick paint and can be applied up to 30 mils per coat. Theoretical coverage at 40 mils is 32 cubic inches per kg. Although one coat will usually provide the required coverage, two or more coats will aid in the control of pinholes and holidays.|
|Mixing & Application|
Mix ALL of Part A with ALL of Part B. Mixing may be done in a container large enough to hold both the base and hardener. The selected container must be clean and dry. Mix the material thoroughly until no streaks of any kind are visible. If materials are cold, warm them to 70 F before mixing.
For best results, do not apply:
|Force cures are recommended for severe service conditions as both the physical and chemical properties are enhanced. Force curing should not start until material has firmly set.|
Recommended Force Cure Schedule:
|Health and Safety|
|READ AND UNDERSTAND ALL MATERIAL GIVEN IN THE MSDS SHEETS BEFORE USING THE PRODUCT.|
EAC DOES NOT CONTAIN ANY FLAMMABLE MATERIAL OF ANY KIND. HOWEVER, THE MATERIAL IS COMBUSTIBLE. IN THE EVENT OF A FIRE, DRY POWDER, FOAM, OR CARBON DIOXIDE FIRE EXTINGUISHERS SHOULD BE USED. FIRE FIGHTERS SHOULD WEAR RESPIRATORS.
USE PROTECTIVE GLOVES AND EYEGLASSES WHEN USING.
USE IN AREAS OF GOOD VENTILATION.
|All recommendations covering the use of this product are based on past experience and laboratory findings. Methods or conditions of application and use of the product are beyond our control. We assume responsibility only for the uniformity of our product within normal manufacturing balances.|
EAC Ceramic Putty
EAC is a brushable and versatile abrasion resistant coating, which has excellent resistance to both acids and caustics as well as having excellent abrasion resistance. It is primarily used to resurface any component requiring both abrasion and chemical resistance such as tanks, heat exchangers, valve or pump internals.