|Resistant to sulfuric acid exposure at concentrations ranging from 5-percent to 98-percent.
Moderately resistant to other acids except hydrofluoric.
Resistant to hydrocarbon, chloride, and sulfate exposure degradation.
Resistant to solvent exposure.
Can be colored.
Utilized at slumps ranging from 1 to 9 inches.
Fiber reinforced (micro).
Interior and exterior applications.
Resistant to freeze and thaw cycles.
Can be used in hot or cold climates.
Improves corrosion protection when placed on metal features.
Supplied in Super Sacks, 55-lb bags, or Ready Mixed Concrete delivery.
|A200 is used in most any pneumatic or conventionally placed concrete applications where the completed feature will be subject to sulfur, sulfuric acid, or many other chemicals in very hot or very cold climates. A200 is many times utilized in the Petrochemical, Fertilizer, Food & Beverage, Mining, and Foundry Industries, and, the Oil & Gas Industry including off-shore drilling platforms due to its chemical resistance and complete resistance to chloride and sulfate attack.|
|140 lbs/ft3 wet density.
6,000 psi typical 28-day compressive strength at a water to cement ratio of 0.32, and a slump of 8 inches.
6,000 psi typical compressive strength in from 4 to 8 hours when subjected to cure temperatures greater than 120 degrees Fahrenheit.
8,000 psi typical 28-day compressive strength at a water to cement ratio of 0.27, and a slump of 5 inches.
Heat resistance up to a sustained 1,000 degrees Fahrenheit, or brief higher temperature exposure.
|Wet Density||140 lb/ft|
|Heat Resistance||Up to 1000 F|
|A200 complies with building code requirements for interaction with conventional reinforcing steel, strength, and modulus properties, but does not comply with typical industry Portland Cement specifications due to the absence of Portland Cement. Cost savings combined with superior quality is not just a goal, it’s inherent with A200.|
A200 Geopolymer Concrete
GEOPOLYMER-A200 (A200) is a 3/8-inch nominal (or other size) aggregate (quartzite) Geopolymer concrete material designed for resistance to sulfuric acid and general purpose use. A200 is resistant to degradation in various concentrations of sulfuric acid ranging from 5-percent to 98-percent with little to no mass loss. A200 can be utilized in low or high slump applications for construction of secondary containment, various feature construction such as drain systems, foundations, walls, flatwork, and every other application typically observed with Portland Cement mixtures.